High impact and puncture resistance
Excellent on-pallet load elongation for higher yields on regular loads
Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a
Information provided by Dow
Dow ELITE™ 5220G Enhanced Polyethylene Resin 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 0.915 g/cc | 0.0331 lb/in³ | ASTM D792 |
| 厚度 | 20.3 microns | 0.800 mil | |
| 熔体流动速率 | 3.5 g/10 min | 3.5 g/10 min | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(MD : 屈服) | 8.96 MPa | 1300 psi | ASTM D882 |
| 抗张强度(TD : 屈服) | 8.41 MPa | 1220 psi | ASTM D882 |
| 断裂伸长率，MD | 450 % | 450 % | ASTM D882 |
| 断裂伸长率，TD | 650 % | 650 % | ASTM D882 |
| 伸长率 (断裂) | 300 % | 300 % | on-pallet testing determined by LANTECH SHS Tester: Ultimate Stretch; Dow Method |
| 冲击 | 10 | 10 | [lb<sub>f</sub>]; Puncture Resistance Force; Dow Method |
| 49 | 49 | [N]; Puncture at 250% pre-stretch; on-pallet testing determined by LANTECH SHS Tester; Dow Method | |
| 323 | 323 | [ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method | |
| 多轴向仪器化冲击能量 | 4.07 J | 3.00 ft-lb | Dow Method |
| 埃尔曼多夫抗撕强度(MD) | 390 g | 390 g | ASTM D1922 |
| 埃尔曼多夫抗撕强度(TD) | 600 g | 600 g | ASTM D1922 |
| 埃尔曼多夫抗撕强度(MD) | 19.19 g/micron | 487.5 g/mil | ASTM D1922 |
| 埃尔曼多夫抗撕强度(TD) | 29.5 g/micron | 750 g/mil | ASTM D1922 |
| 落锤试验 | 630 g | 1.39 lb | Method B; ASTM D1709 |
| 抗张强度(MD : 断裂) | 40.0 MPa | 5800 psi | ASTM D882 |
| 抗张强度(TD : 断裂) | 35.9 MPa | 5200 psi | ASTM D882 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 熔融温度 | 123 °C | 253 °F | Dow Method (DSC) |
| 维卡软化温度 | 99.0 °C | 210 °F | ASTM D1525 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 雾度 | 0.60 % | 0.60 % | ASTM D1003 |
| 光泽度 | 96 % | 96 % | 45°; ASTM D2457 |