| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | 
  | 基本性能 | 密度 |  | ASTM D-792 | 0.922 | g/m3 | 
  | 熔体流动速率 | 190℃/2.16kg | ISO 1133 | 4.1 | g/10min | 
  | 物理性能 | 成型收缩率 | 220℃ | ASTM D-955 | 3 | % | 
  | 机械性能 | 环境开裂应力 | 50℃,0.5% Antarox,Compression Molded | ASTM D-1693 | 4 | hr | 
  | 拉伸模量 | 2% Secant,Extrusion Coating | ASTM D-638 | 204 | MPa | 
  | 拉伸屈服强度 | Compression Molded | ASTM D-638 |  | MPa | 
  | 拉伸断裂强度 | Compression Molded | ASTM D-638 |  | MPa | 
  | 拉伸断裂伸长率 | Compression Molded | ASTM D-638 |  | % | 
  | 弯曲模量 | 2% Secant,Compression Molded | ASTM D-790 | 230 | MPa | 
  | 拉伸冲击强度 | Compression Molded | ASTM D-1822 | 100 | kJ/m2 | 
  | 邵氏硬度 | Shore D,Compression Molded | ASTM D-2240 | 51 |  | 
  | 加工性能 | 熔体温度 |  |  | 270-335 | ℃ | 
  | 热性能 | 维卡软化点 |  | ASTM D-1525 | 98 | ℃ | 
  | 熔化温度 |  | DSC | 110 | ℃ | 
  | 其它性能 | 螺旋流动长度 | 220℃,2 seconds injection | Internal Method | 940 | mm | 
  | 密封起始温度四 |  | Internal Method | 110 | ℃ | 
  | 水汽传输五日 |  | ASTM E-398-83 | 240 | g/m2/24 hr |