| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.900 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/2.16kg) |
|
ASTMD1238 |
8.0 |
g/10min |
| 机械性能 |
抗张强度2(屈服) |
|
ASTMD638 |
25.0 |
MPa |
| 机械性能 |
伸长率2(断裂) |
|
ASTMD638 |
>500 |
% |
| 机械性能 |
弯曲模量 |
|
ASTMD790 |
900 |
MPa |
| 机械性能 |
CoefficientofFriction(Static,CastFilm) |
|
ASTMD1894 |
<0.20 |
|
| 薄膜 |
薄膜厚度-经测试 |
|
|
30 |
µm |
| 薄膜 |
TensileStrength-MD(Break,30µm,CastFilm) |
|
ASTMD882 |
43.1 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,30µm,CastFilm) |
|
ASTMD882 |
33.3 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,30µm,CastFilm) |
|
ASTMD882 |
>500 |
% |
| 薄膜 |
TensileElongation-TD(Break,30µm,CastFilm) |
|
ASTMD882 |
>500 |
% |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C) |
|
ASTMD256 |
49 |
J/m |
| 硬度 |
洛氏硬度(R级) |
|
ASTMD785 |
82 |
|
| 热性能 |
载荷下热变形温度(0.45MPa,未退火) |
|
ASTMD648 |
80.0 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD15253 |
134 |
°C |
| 光学性能 |
Gloss(30.0µm,CastFilm) |
|
ASTMD2457 |
132 |
|
| 光学性能 |
Haze(30.0µm,CastFilm) |
|
ASTMD1003 |
1.5 |
% |
| ADDITIONAL INFORMATION |
补充信息 |
|
TestMethod |
NominalValue |
Unit |
| ADDITIONAL INFORMATION |
HeatSealTemperature4 |
|
InternalMethod |
130 |
°C |