性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
物理性能 |
比重 |
|
ASTMD792 |
1.06 |
g/cm³ |
物理性能 |
密度 |
|
ISO1183 |
1.06 |
g/cm³ |
ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
ELASTOMERS |
拉伸应力-横向流量(100%应变,23°C) |
|
ASTMD412 |
2.10 |
MPa |
ELASTOMERS |
拉伸应力-横向流量(100%应变,23°C) |
|
ISO37 |
2.10 |
MPa |
ELASTOMERS |
抗张强度-横向流量(断裂,23°C) |
|
ASTMD412 |
8.00 |
MPa |
ELASTOMERS |
TensileStress-AcrossFlow(Break,23°C) |
|
ISO37 |
8.00 |
MPa |
ELASTOMERS |
伸长率-横向流量(断裂,23°C) |
|
ASTMD412 |
540 |
% |
ELASTOMERS |
伸长率-横向流量(断裂,23°C) |
|
ISO37 |
540 |
% |
ELASTOMERS |
撕裂强度-横向流量2(23°C) |
|
ASTMD624 |
28.0 |
kN/m |
ELASTOMERS |
TearStrength-AcrossFlow3(23°C) |
|
ISO34-1 |
28 |
kN/m |
ELASTOMERS |
CompressionSet4 |
23°C,22hr |
ASTMD395B |
34 |
% |
ELASTOMERS |
CompressionSet4 |
70°C,22hr |
ASTMD395B |
62 |
% |
ELASTOMERS |
压缩永久变形4 |
23°C,22hr |
ISO815 |
34 |
% |
ELASTOMERS |
压缩永久变形4 |
70°C,22hr |
ISO815 |
62 |
% |
硬度 |
肖氏硬度(邵氏A,15秒,23°C) |
|
ISO868 |
65 |
|
老化 |
ChangeinTensileStrengthinAir(100°C,168hr) |
|
ASTMD573 |
0.0 |
% |
老化 |
ChangeinTensileStrengthinAir(100°C,168hr) |
|
ISO188 |
0.0 |
% |
老化 |
ChangeinUltimateElongationinAir(100°C,168hr) |
|
ASTMD573 |
-11 |
% |
老化 |
ChangeinTensileStrainatBreakinAir(100°C,168hr) |
|
ISO188 |
-11 |
% |
老化 |
ChangeinDurometerHardnessinAir(ShoreA,100°C,672hr) |
|
ASTMD573 |
-2.0 |
|
老化 |
ChangeinShoreHardnessinAir(ShoreA,100°C,672hr) |
|
ISO188 |
-2.0 |
|
老化 |
ChangeinMassinAir(100°C,168hr) |
|
ASTMD573 |
-1.1 |
% |
老化 |
ChangeinMassinAir(100°C,168hr) |
|
ISO188 |
-1.1 |
% |
老化 |
ChangeinVolumeinAir(100°C,168hr) |
|
ASTMD573 |
-1.2 |
% |
老化 |
ChangeinVolumeinAir(100°C,168hr) |
|
ISO188 |
-1.2 |
% |
老化 |
拉伸强度的变化率 |
23°C,24hr,inIRM903Oil |
ASTMD471 |
-4.0 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inCascadeDetergent |
ASTMD471 |
-20 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inClorox,10% |
ASTMD471 |
-16 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inEthanol,50% |
ASTMD471 |
-65 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inHydrochloricAcid,10% |
ASTMD471 |
-20 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inRelativeHumidity,90% |
ASTMD471 |
-11 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inSodiumChloride,15% |
ASTMD471 |
-18 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inSodiumHydroxide,50% |
ASTMD471 |
-22 |
% |
老化 |
拉伸强度的变化率 |
38°C,168hr,inRelativeHumidity,90% |
ASTMD471 |
-16 |
% |
老化 |
拉伸强度的变化率 |
23°C,24hr,inIRM903Oil |
ISO1817 |
-4.0 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inCascadeDetergent |
ISO1817 |
-20 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inClorox,10% |
ISO1817 |
-16 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inEthanol,50% |
ISO1817 |
-65 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inHydrochloricAcid,10% |
ISO1817 |
-20 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inRelativeHumidity,90% |
ISO1817 |
-11 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inSodiumChloride,15% |
ISO1817 |
-18 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inSodiumHydroxide,50% |
ISO1817 |
-22 |
% |
老化 |
拉伸强度的变化率 |
38°C,168hr,inRelativeHumidity,90% |
ISO1817 |
-16 |
% |
老化 |
极限伸长率的变化率 |
23°C,24hr,inIRM903Oil |
ASTMD471 |
-4.0-4.0-4.0-4.0-4.0 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inCascadeDetergent |
ASTMD471 |
-7.0 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inClorox,10% |
ASTMD471 |
-4.0 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inEthanol,50% |
ASTMD471 |
-66 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inHydrochloricAcid,10% |
ASTMD471 |
-10 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inRelativeHumidity,90% |
ASTMD471 |
-10 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inSodiumChloride,15% |
ASTMD471 |
-6.0 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inSodiumHydroxide,50% |
ASTMD471 |
-18 |
% |
老化 |
极限伸长率的变化率 |
38°C,168hr,inRelativeHumidity,90% |
ASTMD471 |
-9.0 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,24hr,inIRM903Oil |
ISO1817 |
-4.0-4.0-4.0-4.0-4.0 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inCascadeDetergent |
ISO1817 |
-7.0 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inClorox,10% |
ISO1817 |
-4.0 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inEthanol,50% |
ISO1817 |
-66 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inHydrochloricAcid,10% |
ISO1817 |
-10 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inRelativeHumidity,90% |
ISO1817 |
-10 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inSodiumChloride,15% |
ISO1817 |
-6.0 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inSodiumHydroxide,50% |
ISO1817 |
-18 |
% |
老化 |
断裂时拉伸应力变化 |
38°C,168hr,inRelativeHumidity,90% |
ISO1817 |
-9.0 |
% |
老化 |
ChangeinDurometerHardness(ShoreA,23°C,168hr,inDeionizedWater) |
|
ASTMD471 |
-1.0 |
|
老化 |
ChangeinShoreHardness(ShoreA,23°C,168hr,inDeionizedWater) |
|
ISO1817 |
-1.0 |
|
老化 |
质量变化率 |
23°C,168hr,inCascadeDetergent |
ASTMD471 |
0.10 |
% |
老化 |
质量变化率 |
23°C,168hr,inClorox,10% |
ASTMD471 |
0.60 |
% |
老化 |
质量变化率 |
23°C,168hr,inEthanol,50% |
ASTMD471 |
6.5 |
% |
老化 |
质量变化率 |
23°C,168hr,inHydrochloricAcid,10% |
ASTMD471 |
0.40 |
% |
老化 |
质量变化率 |
23°C,168hr,inRelativeHumidity,95% |
ASTMD471 |
0.0 |
% |
老化 |
质量变化率 |
23°C,168hr,inSodiumChloride,15% |
ASTMD471 |
0.10 |
% |
老化 |
质量变化率 |
23°C,168hr,inSodiumHydroxide,50% |
ASTMD471 |
0.10 |
% |
老化 |
质量变化率 |
38°C,168hr,inRelativeHumidity,95% |
ASTMD471 |
0.60 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inRelativeHumidity,95% |
ISO1817 |
0.0 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inSodiumChloride,15% |
ISO1817 |
0.10 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inCascadeDetergent |
ISO1817 |
0.10 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inSodiumHydroxide,50% |
ISO1817 |
0.10 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inHydrochloricAcid,10% |
ISO1817 |
0.40 |
% |
老化 |
质量变化率 |
38.0°C,168hr,inRelativeHumidity,95% |
ISO1817 |
0.60 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inClorox,10% |
ISO1817 |
0.60 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inEthanol,50% |
ISO1817 |
6.5 |
% |
老化 |
体积变化 |
23°C,168hr,inCascadeDetergent |
ASTMD471 |
0.10 |
% |
老化 |
体积变化 |
23°C,168hr,inClorox,10% |
ASTMD471 |
0.60 |
% |
老化 |
体积变化 |
23°C,168hr,inEthanol,50% |
ASTMD471 |
6.8 |
% |
老化 |
体积变化 |
23°C,168hr,inHydrochloricAcid,10% |
ASTMD471 |
0.40 |
% |
老化 |
体积变化 |
23°C,168hr,inRelativeHumidity,95% |
ASTMD471 |
0.0 |
% |
老化 |
体积变化 |
23°C,168hr,inSodiumChloride,15% |
ASTMD471 |
0.60 |
% |
老化 |
体积变化 |
23°C,168hr,inSodiumHydroxide,50% |
ASTMD471 |
0.20 |
% |
老化 |
体积变化 |
38°C,168hr,inRelativeHumidity,95% |
ASTMD471 |
0.60 |
% |
老化 |
体积变化 |
23°C,168hr,inCascadeDetergent |
ISO1817 |
0.10 |
% |
老化 |
体积变化 |
23°C,168hr,inClorox,10% |
ISO1817 |
0.60 |
% |
老化 |
体积变化 |
23°C,168hr,inEthanol,50% |
ISO1817 |
6.8 |
% |
老化 |
体积变化 |
23°C,168hr,inHydrochloricAcid,10% |
ISO1817 |
0.40 |
% |
老化 |
体积变化 |
23°C,168hr,inRelativeHumidity,95% |
ISO1817 |
0.0 |
% |
老化 |
体积变化 |
23°C,168hr,inSodiumChloride,15% |
ISO1817 |
0.60 |
% |
老化 |
体积变化 |
23°C,168hr,inSodiumHydroxide,50% |
ISO1817 |
0.20 |
% |
老化 |
体积变化 |
38°C,168hr,inRelativeHumidity,95% |
ISO1817 |
0.60 |
% |