性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
物理性能 |
比重 |
|
ASTMD792 |
0.928 |
g/cm³ |
物理性能 |
密度 |
|
ISO1183 |
0.930 |
g/cm³ |
ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
ELASTOMERS |
拉伸应力-横向流量(100%应变,23°C) |
|
ASTMD412 |
1.00 |
MPa |
ELASTOMERS |
拉伸应力-横向流量(100%应变,23°C) |
|
ISO37 |
1.00 |
MPa |
ELASTOMERS |
抗张强度-横向流量(断裂,23°C) |
|
ASTMD412 |
2.90 |
MPa |
ELASTOMERS |
TensileStress-AcrossFlow(Break,23°C) |
|
ISO37 |
2.90 |
MPa |
ELASTOMERS |
伸长率-横向流量(断裂,23°C) |
|
ASTMD412 |
330 |
% |
ELASTOMERS |
伸长率-横向流量(断裂,23°C) |
|
ISO37 |
330 |
% |
ELASTOMERS |
撕裂强度-横向流量2(23°C) |
|
ASTMD624 |
10.0 |
kN/m |
ELASTOMERS |
TearStrength-AcrossFlow3(23°C) |
|
ISO34-1 |
10 |
kN/m |
ELASTOMERS |
CompressionSet4 |
23°C,22hr |
ASTMD395B |
10 |
% |
ELASTOMERS |
CompressionSet4 |
125°C,70hr |
ASTMD395B |
31 |
% |
ELASTOMERS |
压缩永久变形4 |
23°C,22hr |
ISO815 |
10 |
% |
ELASTOMERS |
压缩永久变形4 |
125°C,70hr |
ISO815 |
31 |
% |
硬度 |
肖氏硬度(邵氏A,15秒,23°C) |
|
ISO868 |
38 |
|
热性能 |
脆化温度 |
|
ASTMD746 |
-63.0 |
°C |
热性能 |
脆化温度 |
|
ISO812 |
-63.0 |
°C |
老化 |
空气中拉伸强度的变化率(150°C,168hr) |
|
ASTMD573 |
-29 |
% |
老化 |
空气中拉伸强度的变化率(150°C,168hr) |
|
ISO188 |
-29 |
% |
老化 |
空气中极限伸长率的变化率(150°C,168hr) |
|
ASTMD573 |
-1.0 |
% |
老化 |
ChangeinTensileStrainatBreakinAir(150°C,168hr) |
|
ISO188 |
-1.0 |
% |
老化 |
ChangeinDurometerHardnessinAir(ShoreA,150°C,168hr) |
|
ASTMD573 |
-1.0 |
|
老化 |
ChangeinShoreHardnessinAir(ShoreA,150°C,168hr) |
|
ISO188 |
-1.0 |
|
老化 |
拉伸强度的变化率 |
23°C,168hr,inAceticAcid |
ASTMD471 |
-6.0 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inCyclohexane |
ASTMD471 |
4040 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inDetergent(Tide),2.5% |
ASTMD471 |
-6.0 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inEthanol,95% |
ASTMD471 |
-8.0 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inHydrochloricAcid,10% |
ASTMD471 |
-6.0 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inIsopropylAlcohol |
ASTMD471 |
27 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inMethylethylketone |
ASTMD471 |
43 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inSodiumChloride,15% |
ASTMD471 |
-14 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inSodiumHydroxide,50% |
ASTMD471 |
-5.0 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inSulfuricAcid,98% |
ASTMD471 |
-47 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inTrichloroethylene |
ASTMD471 |
56 |
% |
老化 |
拉伸强度的变化率 |
100°C,168hr,inDeionizedWater |
ASTMD471 |
-18 |
% |
老化 |
拉伸强度的变化率 |
100°C,168hr,inIRM903Oil |
ASTMD471 |
-57 |
% |
老化 |
拉伸强度的变化率 |
125°C,70hr,inIRM903Oil |
ASTMD471 |
-61 |
% |
老化 |
拉伸强度的变化率 |
125°C,168hr,inIRM903Oil |
ASTMD471 |
-67 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inAceticAcid |
ISO1817 |
-6.0 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inCyclohexane |
ISO1817 |
4040 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inDetergent(Tide),2.5% |
ISO1817 |
-6.0 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inEthanol,95% |
ISO1817 |
-8.0 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inHydrochloricAcid,10% |
ISO1817 |
-6.0 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inIsopropylAlcohol |
ISO1817 |
27 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inMethylethylketone |
ISO1817 |
43 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inSodiumChloride,15% |
ISO1817 |
-14 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inSodiumHydroxide,50% |
ISO1817 |
-5.0 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inSulfuricAcid,98% |
ISO1817 |
-47 |
% |
老化 |
拉伸强度的变化率 |
23°C,168hr,inTrichloroethylene |
ISO1817 |
56 |
% |
老化 |
拉伸强度的变化率 |
100°C,168hr,inDeionizedWater |
ISO1817 |
-18 |
% |
老化 |
拉伸强度的变化率 |
100°C,168hr,inIRM903Oil |
ISO1817 |
-57 |
% |
老化 |
拉伸强度的变化率 |
125°C,70hr,inIRM903Oil |
ISO1817 |
-61 |
% |
老化 |
拉伸强度的变化率 |
125°C,168hr,inIRM903Oil |
ISO1817 |
-67 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inAceticAcid |
ASTMD471 |
-3.0 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inCyclohexane |
ASTMD471 |
63 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inDetergent(Tide),2.5% |
ASTMD471 |
0.0 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inEthanol,95% |
ASTMD471 |
3.0 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inHydrochloricAcid,10% |
ASTMD471 |
0.0 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inIsopropylAlcohol |
ASTMD471 |
53 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inMethylethylketone |
ASTMD471 |
80 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inSodiumChloride,15% |
ASTMD471 |
-7.0 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inSodiumHydroxide,50% |
ASTMD471 |
-3.0 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inSulfuricAcid,98% |
ASTMD471 |
-10 |
% |
老化 |
极限伸长率的变化率 |
23°C,168hr,inTrichloroethylene |
ASTMD471 |
77 |
% |
老化 |
极限伸长率的变化率 |
100°C,168hr,inDeionizedWater |
ASTMD471 |
-17 |
% |
老化 |
极限伸长率的变化率 |
100°C,168hr,inIRM903Oil |
ASTMD471 |
-63 |
% |
老化 |
极限伸长率的变化率 |
125°C,70hr,inIRM903Oil |
ASTMD471 |
-65 |
% |
老化 |
极限伸长率的变化率 |
125°C,168hr,inIRM903Oil |
ASTMD471 |
-70 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inAceticAcid |
ISO1817 |
-3.0 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inCyclohexane |
ISO1817 |
63 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inDetergent(Tide),2.5% |
ISO1817 |
0.0 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inEthanol,95% |
ISO1817 |
3.0 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inHydrochloricAcid,10% |
ISO1817 |
0.0 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inIsopropylAlcohol |
ISO1817 |
53 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inMethylethylketone |
ISO1817 |
80 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inSodiumChloride,15% |
ISO1817 |
-7.0 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inSodiumHydroxide,50% |
ISO1817 |
-3.0 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inSulfuricAcid,98% |
ISO1817 |
-10 |
% |
老化 |
断裂时拉伸应力变化 |
23°C,168hr,inTrichloroethylene |
ISO1817 |
77 |
% |
老化 |
断裂时拉伸应力变化 |
100°C,168hr,inDeionizedWater |
ISO1817 |
-17 |
% |
老化 |
断裂时拉伸应力变化 |
100°C,168hr,inIRM903Oil |
ISO1817 |
-63 |
% |
老化 |
断裂时拉伸应力变化 |
125°C,70hr,inIRM903Oil |
ISO1817 |
-65 |
% |
老化 |
断裂时拉伸应力变化 |
125°C,168hr,inIRM903Oil |
ISO1817 |
-70 |
% |
老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inAceticAcid |
ASTMD471 |
-1.0 |
|
老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inCyclohexane |
ASTMD471 |
-11 |
|
老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inDetergent(Tide),2.5% |
ASTMD471 |
2.0 |
|
老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inEthanol,95% |
ASTMD471 |
1.0 |
|
老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inHydrochloricAcid,10% |
ASTMD471 |
-1.0 |
|
老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inIsopropylAlcohol |
ASTMD471 |
5.0 |
|
老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inMethylethylketone |
ASTMD471 |
15 |
|
老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inSodiumChloride,15% |
ASTMD471 |
2.0 |
|
老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inSodiumHydroxide,50% |
ASTMD471 |
4.0 |
|
老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inSulfuricAcid,98% |
ASTMD471 |
-2.0 |
|
老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inTrichloroethylene |
ASTMD471 |
1.0 |
|
老化 |
硬度计硬度的变化率2 |
ShoreA,100°C,168hr,inDeionizedWater |
ASTMD471 |
0.0 |
|
老化 |
硬度计硬度的变化率2 |
ShoreA,100°C,168hr,inIRM903Oil |
ASTMD471 |
-26 |
|
老化 |
硬度计硬度的变化率2 |
ShoreA,125°C,168hr,inIRM903Oil |
ASTMD471 |
-30 |
|
老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inAceticAcid |
ISO1817 |
-1.0 |
|
老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inCyclohexane |
ISO1817 |
-11 |
|
老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inDetergent(Tide),2.5% |
ISO1817 |
2.0 |
|
老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inEthanol,95% |
ISO1817 |
1.0 |
|
老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inHydrochloricAcid,10% |
ISO1817 |
-1.0 |
|
老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inIsopropylAlcohol |
ISO1817 |
5.0 |
|
老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inMethylethylketone |
ISO1817 |
15 |
|
老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inSodiumChloride,15% |
ISO1817 |
2.0 |
|
老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inSodiumHydroxide,50% |
ISO1817 |
4.0 |
|
老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inSulfuricAcid,98% |
ISO1817 |
-2.0 |
|
老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inTrichloroethylene |
ISO1817 |
1.0 |
|
老化 |
ChangeinShoreHardness |
ShoreA,100°C,168hr,inDeionizedWater |
ISO1817 |
0.0 |
|
老化 |
ChangeinShoreHardness |
ShoreA,100°C,168hr,inIRM903Oil |
ISO1817 |
-26 |
|
老化 |
ChangeinShoreHardness |
ShoreA,125°C,168hr,inIRM903Oil |
ISO1817 |
-30 |
|
老化 |
质量变化率 |
23°C,168hr,inAceticAcid |
ASTMD471 |
6.9 |
% |
老化 |
质量变化率 |
23°C,168hr,inCyclohexane |
ASTMD471 |
-11 |
% |
老化 |
质量变化率 |
23°C,168hr,inDetergent(Tide),2.5% |
ASTMD471 |
0.90 |
% |
老化 |
质量变化率 |
23°C,168hr,inEthanol,95% |
ASTMD471 |
0.20 |
% |
老化 |
质量变化率 |
23°C,168hr,inHydrochloricAcid,10% |
ASTMD471 |
0.20 |
% |
老化 |
质量变化率 |
23°C,168hr,inIsopropylAlcohol |
ASTMD471 |
-25 |
% |
老化 |
质量变化率 |
23°C,168hr,inMethylethylketone |
ASTMD471 |
-41 |
% |
老化 |
质量变化率 |
23°C,168hr,inSodiumChloride,15% |
ASTMD471 |
0.10 |
% |
老化 |
质量变化率 |
23°C,168hr,inSodiumHydroxide,50% |
ASTMD471 |
-0.30 |
% |
老化 |
质量变化率 |
23°C,168hr,inSulfuricAcid,98% |
ASTMD471 |
7.2 |
% |
老化 |
质量变化率 |
23°C,168hr,inTrichloroethylene |
ASTMD471 |
-20 |
% |
老化 |
质量变化率 |
100°C,168hr,inDeionizedWater |
ASTMD471 |
6.2 |
% |
老化 |
质量变化率 |
100°C,168hr,inIRM903Oil |
ASTMD471 |
93 |
% |
老化 |
质量变化率 |
125°C,168hr,inIRM903Oil |
ASTMD471 |
100 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inMethylethylketone |
ISO1817 |
-41 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inIsopropylAlcohol |
ISO1817 |
-25 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inTrichloroethylene |
ISO1817 |
-20 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inCyclohexane |
ISO1817 |
-11 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inSodiumHydroxide,50% |
ISO1817 |
-0.30 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inSodiumChloride,15% |
ISO1817 |
0.10 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inHydrochloricAcid,10% |
ISO1817 |
0.20 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inEthanol,95% |
ISO1817 |
0.20 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inDetergent(Tide),2.5% |
ISO1817 |
0.90 |
% |
老化 |
质量变化率 |
100°C,168hr,inDeionizedWater |
ISO1817 |
6.2 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inAceticAcid |
ISO1817 |
6.9 |
% |
老化 |
质量变化率 |
23.0°C,168hr,inSulfuricAcid,98% |
ISO1817 |
7.2 |
% |
老化 |
质量变化率 |
100°C,168hr,inIRM903Oil |
ISO1817 |
93 |
% |
老化 |
质量变化率 |
125°C,168hr,inIRM903Oil |
ISO1817 |
100 |
% |
老化 |
体积变化(125°C,70hr,在IRM903油中) |
|
ASTMD471 |
110 |
% |
老化 |
体积变化(125°C,70hr,在IRM903油中) |
|
ISO1817 |
110 |
% |
可燃性 |
UL阻燃等级(1.5mm) |
|
UL94 |
HB |
|