| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.968 |
g/cm³ |
| 物理性能 |
密度 |
|
ISO1183 |
0.970 |
g/cm³ |
| 物理性能 |
DetergentResistance |
|
UL2157 |
f4 |
|
| 物理性能 |
DetergentResistance |
|
UL749 |
f3 |
|
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
拉伸应力-横向流量(100%应变,23°C) |
|
ASTMD412 |
3.60 |
MPa |
| ELASTOMERS |
拉伸应力-横向流量(100%应变,23°C) |
|
ISO37 |
3.60 |
MPa |
| ELASTOMERS |
抗张强度-横向流量(断裂,23°C) |
|
ASTMD412 |
8.80 |
MPa |
| ELASTOMERS |
TensileStress-AcrossFlow(Break,23°C) |
|
ISO37 |
8.80 |
MPa |
| ELASTOMERS |
伸长率-横向流量(断裂,23°C) |
|
ASTMD412 |
490 |
% |
| ELASTOMERS |
伸长率-横向流量(断裂,23°C) |
|
ISO37 |
490 |
% |
| ELASTOMERS |
撕裂强度-横向流量2(23°C) |
|
ASTMD624 |
27.0 |
kN/m |
| ELASTOMERS |
TearStrength-AcrossFlow3(23°C) |
|
ISO34-1 |
27 |
kN/m |
| ELASTOMERS |
CompressionSet4 |
70°C,22hr |
ASTMD395B |
28 |
% |
| ELASTOMERS |
CompressionSet4 |
125°C,70hr |
ASTMD395B |
37 |
% |
| ELASTOMERS |
压缩永久变形4 |
70°C,22hr |
ISO815 |
28 |
% |
| ELASTOMERS |
压缩永久变形4 |
125°C,70hr |
ISO815 |
37 |
% |
| 硬度 |
肖氏硬度(邵氏A,15秒,23°C) |
|
ISO868 |
78 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
-60.0 |
°C |
| 热性能 |
脆化温度 |
|
ISO812 |
-60.0 |
°C |
| 热性能 |
RTIElec |
|
UL746 |
100 |
°C |
| 热性能 |
RTIStr |
1.0mm |
UL746 |
90.0 |
°C |
| 热性能 |
RTIStr |
1.5mm |
UL746 |
90.0 |
°C |
| 热性能 |
RTIStr |
3.0mm |
UL746 |
95.0 |
°C |
| 老化 |
空气中拉伸强度的变化率(150°C,168hr) |
|
ASTMD573 |
-1.0 |
% |
| 老化 |
空气中拉伸强度的变化率(150°C,168hr) |
|
ISO188 |
-1.0 |
% |
| 老化 |
空气中极限伸长率的变化率(150°C,168hr) |
|
ASTMD573 |
-3.0 |
% |
| 老化 |
ChangeinTensileStrainatBreakinAir(150°C,168hr) |
|
ISO188 |
-3.0 |
% |
| 老化 |
ChangeinDurometerHardnessinAir(ShoreA,150°C,168hr) |
|
ASTMD573 |
7.0 |
|
| 老化 |
ChangeinShoreHardnessinAir(ShoreA,150°C,168hr) |
|
ISO188 |
7.0 |
|
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inAceticAcid |
ASTMD471 |
-8.0 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inCyclohexane |
ASTMD471 |
31 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inDetergent(Tide),2.5% |
ASTMD471 |
3.0 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inEthanol,95% |
ASTMD471 |
-2.0 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inHydrochloricAcid,10% |
ASTMD471 |
13 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inIsopropylAlcohol |
ASTMD471 |
31 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inMethylethylketone |
ASTMD471 |
47 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inSodiumChloride,15% |
ASTMD471 |
0.0 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inSodiumHydroxide,50% |
ASTMD471 |
3.0 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inSulfuricAcid,98% |
ASTMD471 |
-17-17 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inTrichloroethylene |
ASTMD471 |
54 |
% |
| 老化 |
拉伸强度的变化率 |
100°C,168hr,inDeionizedWater |
ASTMD471 |
1.0 |
% |
| 老化 |
拉伸强度的变化率 |
100°C,168hr,inIRM903Oil |
ASTMD471 |
-30 |
% |
| 老化 |
拉伸强度的变化率 |
125°C,70hr,inIRM903Oil |
ASTMD471 |
-31 |
% |
| 老化 |
拉伸强度的变化率 |
125°C,168hr,inIRM903Oil |
ASTMD471 |
-31 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inAceticAcid |
ISO1817 |
-8.0 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inCyclohexane |
ISO1817 |
31 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inDetergent(Tide),2.5% |
ISO1817 |
3.0 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inEthanol,95% |
ISO1817 |
-2.0 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inHydrochloricAcid,10% |
ISO1817 |
13 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inIsopropylAlcohol |
ISO1817 |
31 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inMethylethylketone |
ISO1817 |
47 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inSodiumChloride,15% |
ISO1817 |
0.0 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inSodiumHydroxide,50% |
ISO1817 |
3.0 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inSulfuricAcid,98% |
ISO1817 |
-17-17 |
% |
| 老化 |
拉伸强度的变化率 |
23°C,168hr,inTrichloroethylene |
ISO1817 |
54 |
% |
| 老化 |
拉伸强度的变化率 |
100°C,168hr,inDeionizedWater |
ISO1817 |
1.0 |
% |
| 老化 |
拉伸强度的变化率 |
100°C,168hr,inIRM903Oil |
ISO1817 |
-30 |
% |
| 老化 |
拉伸强度的变化率 |
125°C,70hr,inIRM903Oil |
ISO1817 |
-31 |
% |
| 老化 |
拉伸强度的变化率 |
125°C,168hr,inIRM903Oil |
ISO1817 |
-31 |
% |
| 老化 |
极限伸长率的变化率 |
23°C,168hr,inAceticAcid |
ASTMD471 |
-4.0 |
% |
| 老化 |
极限伸长率的变化率 |
23°C,168hr,inCyclohexane |
ASTMD471 |
20 |
% |
| 老化 |
极限伸长率的变化率 |
23°C,168hr,inDetergent(Tide),2.5% |
ASTMD471 |
2.0 |
% |
| 老化 |
极限伸长率的变化率 |
23°C,168hr,inEthanol,95% |
ASTMD471 |
0.0 |
% |
| 老化 |
极限伸长率的变化率 |
23°C,168hr,inHydrochloricAcid,10% |
ASTMD471 |
9.0 |
% |
| 老化 |
极限伸长率的变化率 |
23°C,168hr,inIsopropylAlcohol |
ASTMD471 |
20 |
% |
| 老化 |
极限伸长率的变化率 |
23°C,168hr,inMethylethylketone |
ASTMD471 |
24 |
% |
| 老化 |
极限伸长率的变化率 |
23°C,168hr,inSodiumChloride,15% |
ASTMD471 |
-2.0 |
% |
| 老化 |
极限伸长率的变化率 |
23°C,168hr,inSodiumHydroxide,50% |
ASTMD471 |
2.0 |
% |
| 老化 |
极限伸长率的变化率 |
23°C,168hr,inSulfuricAcid,98% |
ASTMD471 |
-27 |
% |
| 老化 |
极限伸长率的变化率 |
23°C,168hr,inTrichloroethylene |
ASTMD471 |
22 |
% |
| 老化 |
极限伸长率的变化率 |
100°C,168hr,inDeionizedWater |
ASTMD471 |
-7.0 |
% |
| 老化 |
极限伸长率的变化率 |
100°C,168hr,inIRM903Oil |
ASTMD471 |
-49 |
% |
| 老化 |
极限伸长率的变化率 |
125°C,70hr,inIRM903Oil |
ASTMD471 |
-47 |
% |
| 老化 |
极限伸长率的变化率 |
125°C,168hr,inIRM903Oil |
ASTMD471 |
-58 |
% |
| 老化 |
断裂时拉伸应力变化 |
23°C,168hr,inAceticAcid |
ISO1817 |
-4.0 |
% |
| 老化 |
断裂时拉伸应力变化 |
23°C,168hr,inCyclohexane |
ISO1817 |
20 |
% |
| 老化 |
断裂时拉伸应力变化 |
23°C,168hr,inDetergent(Tide),2.5% |
ISO1817 |
2.0 |
% |
| 老化 |
断裂时拉伸应力变化 |
23°C,168hr,inEthanol,95% |
ISO1817 |
0.0 |
% |
| 老化 |
断裂时拉伸应力变化 |
23°C,168hr,inHydrochloricAcid,10% |
ISO1817 |
9.0 |
% |
| 老化 |
断裂时拉伸应力变化 |
23°C,168hr,inIsopropylAlcohol |
ISO1817 |
20 |
% |
| 老化 |
断裂时拉伸应力变化 |
23°C,168hr,inMethylethylketone |
ISO1817 |
24 |
% |
| 老化 |
断裂时拉伸应力变化 |
23°C,168hr,inSodiumChloride,15% |
ISO1817 |
-2.0 |
% |
| 老化 |
断裂时拉伸应力变化 |
23°C,168hr,inSodiumHydroxide,50% |
ISO1817 |
2.0 |
% |
| 老化 |
断裂时拉伸应力变化 |
23°C,168hr,inSulfuricAcid,98% |
ISO1817 |
-27 |
% |
| 老化 |
断裂时拉伸应力变化 |
23°C,168hr,inTrichloroethylene |
ISO1817 |
22 |
% |
| 老化 |
断裂时拉伸应力变化 |
100°C,168hr,inDeionizedWater |
ISO1817 |
-7.0 |
% |
| 老化 |
断裂时拉伸应力变化 |
100°C,168hr,inIRM903Oil |
ISO1817 |
-49 |
% |
| 老化 |
断裂时拉伸应力变化 |
125°C,70hr,inIRM903Oil |
ISO1817 |
-47 |
% |
| 老化 |
断裂时拉伸应力变化 |
125°C,168hr,inIRM903Oil |
ISO1817 |
-58 |
% |
| 老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inAceticAcid |
ASTMD471 |
-2.0 |
|
| 老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inCyclohexane |
ASTMD471 |
-16 |
|
| 老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inDetergent(Tide),2.5% |
ASTMD471 |
0.0 |
|
| 老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inEthanol,95% |
ASTMD471 |
0.0 |
|
| 老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inHydrochloricAcid,10% |
ASTMD471 |
-3.0 |
|
| 老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inIsopropylAlcohol |
ASTMD471 |
-1.0 |
|
| 老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inMethylethylketone |
ASTMD471 |
0.0 |
|
| 老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inSodiumChloride,15% |
ASTMD471 |
0.0 |
|
| 老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inSodiumHydroxide,50% |
ASTMD471 |
0.0 |
|
| 老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inSulfuricAcid,98% |
ASTMD471 |
0.0 |
|
| 老化 |
硬度计硬度的变化率2 |
ShoreA,23°C,168hr,inTrichloroethylene |
ASTMD471 |
-3.0 |
|
| 老化 |
硬度计硬度的变化率2 |
ShoreA,100°C,168hr,inDeionizedWater |
ASTMD471 |
-2.0 |
|
| 老化 |
硬度计硬度的变化率2 |
ShoreA,100°C,168hr,inIRM903Oil |
ASTMD471 |
-21 |
|
| 老化 |
硬度计硬度的变化率2 |
ShoreA,125°C,168hr,inIRM903Oil |
ASTMD471 |
-23 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inAceticAcid |
ISO1817 |
-2.0 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inCyclohexane |
ISO1817 |
-16 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inDetergent(Tide),2.5% |
ISO1817 |
0.0 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inEthanol,95% |
ISO1817 |
0.0 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inHydrochloricAcid,10% |
ISO1817 |
-3.0 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inIsopropylAlcohol |
ISO1817 |
-1.0 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inMethylethylketone |
ISO1817 |
0.0 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inSodiumChloride,15% |
ISO1817 |
0.0 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inSodiumHydroxide,50% |
ISO1817 |
0.0 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inSulfuricAcid,98% |
ISO1817 |
0.0 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,23°C,168hr,inTrichloroethylene |
ISO1817 |
-3.0 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,100°C,168hr,inDeionizedWater |
ISO1817 |
-2.0 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,100°C,168hr,inIRM903Oil |
ISO1817 |
-21 |
|
| 老化 |
ChangeinShoreHardness |
ShoreA,125°C,168hr,inIRM903Oil |
ISO1817 |
-23 |
|
| 老化 |
质量变化率 |
23°C,168hr,inAceticAcid |
ASTMD471 |
4.0 |
% |
| 老化 |
质量变化率 |
23°C,168hr,inCyclohexane |
ASTMD471 |
-4.9 |
% |
| 老化 |
质量变化率 |
23°C,168hr,inDetergent(Tide),2.5% |
ASTMD471 |
0.60 |
% |
| 老化 |
质量变化率 |
23°C,168hr,inEthanol,95% |
ASTMD471 |
-0.10 |
% |
| 老化 |
质量变化率 |
23°C,168hr,inHydrochloricAcid,10% |
ASTMD471 |
0.20 |
% |
| 老化 |
质量变化率 |
23°C,168hr,inIsopropylAlcohol |
ASTMD471 |
-13 |
% |
| 老化 |
质量变化率 |
23°C,168hr,inMethylethylketone |
ASTMD471 |
-24 |
% |
| 老化 |
质量变化率 |
23°C,168hr,inSodiumChloride,15% |
ASTMD471 |
0.20 |
% |
| 老化 |
质量变化率 |
23°C,168hr,inSodiumHydroxide,50% |
ASTMD471 |
-0.20 |
% |
| 老化 |
质量变化率 |
23°C,168hr,inTrichloroethylene |
ASTMD471 |
-6.0 |
% |
| 老化 |
质量变化率 |
100°C,168hr,inDeionizedWater |
ASTMD471 |
3.6 |
% |
| 老化 |
质量变化率 |
100°C,168hr,inIRM903Oil |
ASTMD471 |
66 |
% |
| 老化 |
质量变化率 |
125°C,168hr,inIRM903Oil |
ASTMD471 |
78 |
% |
| 老化 |
质量变化率 |
23.0°C,168hr,inMethylethylketone |
ISO1817 |
-24 |
% |
| 老化 |
质量变化率 |
23.0°C,168hr,inIsopropylAlcohol |
ISO1817 |
-13 |
% |
| 老化 |
质量变化率 |
23.0°C,168hr,inTrichloroethylene |
ISO1817 |
-6.0 |
% |
| 老化 |
质量变化率 |
23.0°C,168hr,inCyclohexane |
ISO1817 |
-4.9 |
% |
| 老化 |
质量变化率 |
23.0°C,168hr,inSodiumHydroxide,50% |
ISO1817 |
-0.20 |
% |
| 老化 |
质量变化率 |
23.0°C,168hr,inEthanol,95% |
ISO1817 |
-0.10 |
% |
| 老化 |
质量变化率 |
23.0°C,168hr,inHydrochloricAcid,10% |
ISO1817 |
0.20 |
% |
| 老化 |
质量变化率 |
23.0°C,168hr,inSodiumChloride,15% |
ISO1817 |
0.20 |
% |
| 老化 |
质量变化率 |
23.0°C,168hr,inDetergent(Tide),2.5% |
ISO1817 |
0.60 |
% |
| 老化 |
质量变化率 |
100°C,168hr,inDeionizedWater |
ISO1817 |
3.6 |
% |
| 老化 |
质量变化率 |
23.0°C,168hr,inAceticAcid |
ISO1817 |
4.0 |
% |
| 老化 |
质量变化率 |
100°C,168hr,inIRM903Oil |
ISO1817 |
66 |
% |
| 老化 |
质量变化率 |
125°C,168hr,inIRM903Oil |
ISO1817 |
78 |
% |
| 老化 |
体积变化(125°C,70hr,在IRM903油中) |
|
ASTMD471 |
72 |
% |
| 老化 |
体积变化(125°C,70hr,在IRM903油中) |
|
ISO1817 |
72 |
% |
| 老化 |
ContinuousUpperTemperatureResistance(1008hr) |
|
SAEJ2236 |
135 |
°C |
| 电气性能 |
DielectricStrength(23°C,2.00mm) |
|
ASTMD149 |
30 |
kV/mm |
| 电气性能 |
DielectricConstant(23°C,1.96mm) |
|
ASTMD150 |
2.40 |
|
| 电气性能 |
DielectricConstant(23°C,1.96mm) |
|
IEC60250 |
2.40 |
|
| 电气性能 |
相比耐漏电起痕指数(CTI) |
|
UL746 |
PLC0 |
|
| 电气性能 |
高电弧燃烧指数(HAI) |
|
UL746 |
PLC0 |
|
| 电气性能 |
高压电弧抗点燃指数(HVAR)(PLC) |
|
UL746 |
PLC6 |
|
| 电气性能 |
高电压电弧起痕速率(HVTR) |
|
UL746 |
PLC1 |
|
| 电气性能 |
热丝引燃(HWI) |
1.0mm |
UL746 |
PLC4 |
|
| 电气性能 |
热丝引燃(HWI) |
1.5mm |
UL746 |
PLC3 |
|
| 电气性能 |
热丝引燃(HWI) |
3.0mm |
UL746 |
PLC3 |
|
| 可燃性 |
UL阻燃等级 |
1.0mm |
UL94 |
HB |
|
| 可燃性 |
UL阻燃等级 |
1.5mm |
UL94 |
HB |
|
| 可燃性 |
UL阻燃等级 |
3.0mm |
UL94 |
HB |
|