| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.18 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/2.16kg) |
|
ASTMD1238 |
14 |
g/10min |
| 物理性能 |
MoldingShrinkage-Flow(3.20mm,InjectionMolded) |
|
ASTMD955 |
1.0to1.4 |
% |
| 物理性能 |
吸水率(23°C,24hr) |
|
ASTMD570 |
0.60 |
% |
| 机械性能 |
TensileStrength2(Yield,23°C,2.00mm,InjectionMolded) |
|
ASTMD638 |
13.2 |
MPa |
| 机械性能 |
抗张强度2(断裂,23°C,2.00mm,注塑) |
|
ASTMD638 |
34.3 |
MPa |
| 机械性能 |
伸长率2(断裂,23°C,2.00mm,注塑) |
|
ASTMD638 |
850 |
% |
| 机械性能 |
FlexuralModulus3(23°C,6.40mm,InjectionMolded) |
|
ASTMD790 |
167 |
MPa |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
撕裂强度2(23°C) |
|
ASTMD624 |
147 |
kN/m |
| 冲击性能 |
悬壁梁缺口冲击强度 |
-40°C,6.40mm,注塑 |
ASTMD256 |
250 |
J/m |
| 冲击性能 |
悬壁梁缺口冲击强度 |
23°C,6.40mm,注塑 |
ASTMD256 |
NoBreak |
|
| 硬度 |
DurometerHardness(ShoreD,23°C,InjectionMolded) |
|
ASTMD2240 |
52 |
|
| 热性能 |
载荷下热变形温度(0.45MPa,未退火,6.40mm,注塑) |
|
ASTMD648 |
85.0 |
°C |
| 热性能 |
熔融峰值温度 |
|
ASTMD3418 |
200 |
°C |
| 电气性能 |
体积电阻率(23°C) |
|
ASTMD257 |
>1.0E+13 |
ohms·cm |
| 电气性能 |
介电强度(23°C,1.00mm) |
|
ASTMD149 |
26 |
kV/mm |
| 电气性能 |
漏电起痕指数(解决方案A) |
|
IEC60112 |
600 |
V |