性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
|
物理性能 |
密度 |
|
ASTM D792 |
1.23
|
g/cm³
|
|
|
|
|
ISO 1183 |
1.30 |
g/cm³
|
|
|
熔流率 |
(300°C/1.2 kg) |
ASTM D1238 |
6.5 |
g/10 min
|
|
|
溶化体积流率 |
（MVR） (300°C/1.2 kg) |
ISO 1133 |
6.0 |
cm³/10min
|
|
|
收缩率 |
流动 Tensile Bar |
Internal Method |
0.20 到 0.50
|
%
|
|
|
|
|
Internal Method |
|
%
|
|
|
|
横向流动 : 3.20 mm
|
Internal Method |
0.20 到 0.50
|
%
|
|
|
吸水率
|
|
|
|
%
|
|
|
饱和, 23°C
|
ISO 62 |
0.35
|
%
|
|
|
平衡, 23°C, 50% RH
|
ISO 62 |
0.15
|
%
|
|
|
|
|
|
|
|
|
机械性能 |
拉伸模量
|
5.0 mm/min |
ASTM D638 |
5330
|
MPa
|
|
|
|
ISO 527-2/1 |
4960 |
MPa
|
|
|
抗张强度
|
屈服 类型 1, 50 mm/min |
ASTM D638 |
92.0
|
MPa
|
|
|
|
屈服 |
ISO 527-2/50 |
103 |
MPa
|
|
|
|
断裂 类型 1, 50 mm/min |
ASTM D638 |
91.0 |
MPa
|
|
|
|
断裂 |
ISO 527-2/50 |
101 |
MPa
|
|
|
伸长率
|
屈服 类型 1, 50 mm/min |
ASTM D638 |
3.5 |
%
|
|
|
|
屈服 |
ISO 527-2/50 |
3.7 |
%
|
|
|
|
断裂 类型 1, 50 mm/min |
ASTM D638 |
4.0 |
%
|
|
|
|
断裂 |
ISO 527-2/50 |
4.4 |
%
|
|
|
弯曲模量
|
50.0 mm 跨距,1.3 mm/min |
ASTM D790 |
4600 |
MPa
|
|
|
|
2.0 mm/min |
ISO 178 |
4290 |
MPa
|
|
|
弯曲强度
|
2.0 mm/min,屈服 |
ISO 178 |
150
|
MPa
|
|
|
|
屈服, 50.0 mm 跨距,1.3 mm/min |
ASTM D790 |
156 |
MPa
|
|
冲击性能 |
简支梁缺口冲击强度 |
80*10*3 sp=62mm (23°C) |
ISO 179/1eA |
8.0 |
kJ/m²
|
|
|
|
23°C |
ISO 179/2C |
12 |
kJ/m²
|
|
|
|
-30°C 80*10*3 sp=62mm
|
ISO 179/1eA |
6.0 |
kJ/m²
|
|
|
|
-30°C |
ISO 179/2C |
9.0 |
kJ/m²
|
|
|
简支梁缺口冲击强度 |
80*10*3 sp=62mm (23°C) |
ISO 179/1eU |
100
|
kJ/m²
|
|
|
|
23°C |
ISO 179/2U |
68 |
kJ/m²
|
|
|
|
-30°C 80*10*3 sp=62mm
|
ISO 179/1eU |
100
|
kJ/m²
|
|
|
|
-30°C
|
ISO 179/2U |
76 |
kJ/m²
|
|
|
悬壁梁缺口冲击强度
|
23°C
|
ASTM D256 |
78 |
J/m
|
|
|
|
-30°C,80*10*3
|
ISO 180/1A |
7.0
|
kJ/m²
|
|
|
|
23°C,80*10*3
|
ISO 180/1A |
8.0
|
kJ/m²
|
|
|
无缺口伊佐德冲击强度
|
23°C
|
ISO 180/1U |
80
|
kJ/m²
|
|
|
|
-30°C,80*10*3
|
ISO 180/1U |
80
|
kJ/m²
|
|
|
装有测量仪表的落镖冲击 |
(23°C, Total Energy) |
ASTM D3763 |
61.0 |
J |
|
热性能 |
热变形温度
|
0.45 MPa, 未退火, 3.20 mm
|
ASTM D648 |
145 |
°C
|
|
|
|
|
|
|
|
|
|
|
1.8 MPa, 退火, 3.20 mm
|
ASTM D648 |
141 |
°C
|
|
|
|
1.8 MPa, 未退火, 64.0 mm 跨距,80*10*4 mm |
ISO 75-2/Af |
132 |
°C
|
|
|
维卡软化温度
|
标准 B (120°C/h), 压 力2 (50N) |
ASTM D1525 |
148 |
°C
|
|
|
|
|
ISO 306/B50 |
150 |
°C
|
|
|
|
|
ISO 306/B120 |
151 |
°C
|
|
|
Ball Pressure Test |
125°C |
IEC 60695-10-2 |
Pass |
|
|
|
线形膨胀系数
|
|
ASTM D696 |
|
cm/cm/°C
|
|
|
|
|
ISO 11359-2 |
|
cm/cm/°C
|
|
|
|
|
ASTM D696 |
|
cm/cm/°C
|
|
|
|
横向 : 23 到 80°C
|
ISO 11359-2 |
|
cm/cm/°C
|
|
|
RTI Elec
|
|
UL 746 |
80.0
|
°C
|
|
|
RTI Imp
|
|
UL 746 |
80.0
|
°C
|
|
|
RTI Str
|
|
UL 746 |
80.0
|
°C
|
|
电气性能 |
表面电阻率
|
|
IEC 60093 |
> 1.0E+15
|
ohm
|
|
|
体积电阻率
|
|
IEC 60093 |
> 1.0E+15
|
ohm·cm
|
|
|
介电强度
|
(1.60 mm, in Oil) |
ASTM D149 |
20 |
kV/mm
|
|
|
相对电容率
|
50 Hz
|
IEC 60250 |
|
|
|
|
|
60 Hz
|
IEC 60250 |
|
|
|
|
|
1 MHz
|
IEC 60250 |
|
|
|
|
耗散因数
|
50 Hz
|
IEC 60250 |
|
|
|
|
|
60 Hz
|
IEC 60250 |
|
|
|
|
|
1 MHz
|
IEC 60250 |
0.010
|
|
|
|
漏电起痕指数
|
|
IEC 60112 |
150
|
V |
|
可燃性 |
UL 阻燃等级 |
|
|
|
|
|
|
|
1.50 mm
|
UL 94 |
V-0
|
|
|
|
灼热丝易燃指数
|
(1.00 mm) |
IEC 60695-2-12
|
960 |
°C
|
|
|
热灯丝点火温度
|
(1.00 mm) |
IEC 60695-2-13 |
825 |
°C
|
|
|
极限氧指数
|
|
ISO 4589-2 |
38 |
% |
|
注射 |
干燥温度
|
|
|
120 |
°C
|
|
|
干燥时间
|
|
|
2到4 |
hr
|
|
|
|
|
|
|
|
|
|
建议的最大水分含量
|
|
|
0.02 |
% |
|
|
建议注入量
|
|
|
60到80 |
% |
|
|
螺筒后部温度
|
|
|
270 到 300
|
°C
|
|
|
螺筒中部温度
|
|
|
280 到 310
|
°C
|
|
|
螺筒前部温度
|
|
|
290 到 320
|
°C
|
|
|
射嘴温度
|
|
|
280 到 310
|
°C
|
|
|
加工（熔体）温度
|
|
|
290 到 320
|
°C
|
|
|
模具温度
|
|
|
80.0 到 120
|
°C
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|