DuPont Performance Polymers Zytel® FR70G25V0 NC010 Nylon 66 (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.35 g/cc | 0.0488 lb/in³ | |
| 1.49 g/cc | 0.0538 lb/in³ | DAM; ISO 1183 | |
| 吸水率 | 3.4 % @Thickness 2.00 mm | 3.4 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 水分吸收 | 0.900 % @Thickness 2.00 mm | 0.900 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 粘度 | 85370 cP @Shear Rate 5000 1/s, Temperature 280 °C | 85370 cP @Shear Rate 5000 1/s, Temperature 536 °F | ISO 11403-1 -2 |
| 138900 cP @Shear Rate 5000 1/s, Temperature 270 °C | 138900 cP @Shear Rate 5000 1/s, Temperature 518 °F | ISO 11403-1 -2 | |
| 243400 cP @Shear Rate 5000 1/s, Temperature 260 °C | 243400 cP @Shear Rate 5000 1/s, Temperature 500 °F | ISO 11403-1 -2 | |
| 270750 cP @Shear Rate 500 1/s, Temperature 280 °C | 270750 cP @Shear Rate 500 1/s, Temperature 536 °F | ISO 11403-1 -2 | |
| 441600 cP @Shear Rate 500 1/s, Temperature 270 °C | 441600 cP @Shear Rate 500 1/s, Temperature 518 °F | ISO 11403-1 -2 | |
| 774800 cP @Shear Rate 500 1/s, Temperature 260 °C | 774800 cP @Shear Rate 500 1/s, Temperature 500 °F | ISO 11403-1 -2 | |
| 粘度测试 | 140 cm³/g | 140 cm³/g | DAM; ISO 307 1157 1628 |
| 线性成型收缩率,Flow | 0.0020 cm/cm | 0.0020 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.010 cm/cm | 0.010 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 110 MPa | 16000 psi | 50%RH; ISO 527-1/-2 |
| 125 MPa | 18100 psi | DAM; ISO 527-1/-2 | |
| 抗张强度 | 8.79 MPa @Strain 0.230 %, Temperature 150 °C | 1270 psi @Strain 0.230 %, Temperature 302 °F | DAM; ISO 11403-1 -2 |
| 12.0 MPa @Strain 0.240 %, Temperature 90.0 °C | 1740 psi @Strain 0.240 %, Temperature 194 °F | DAM; ISO 11403-1 -2 | |
| 15.95 MPa @Strain 0.470 %, Temperature 150 °C | 2313 psi @Strain 0.470 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 | |
| 22.76 MPa @Strain 0.480 %, Temperature 90.0 °C | 3301 psi @Strain 0.480 %, Temperature 194 °F | 50%RH; ISO 11403-1 -2 | |
| 24.06 MPa @Strain 0.700 %, Temperature 150 °C | 3490 psi @Strain 0.700 %, Temperature 302 °F | DAM; ISO 11403-1 -2 | |
| 25.92 MPa @Strain 0.400 %, Temperature 40.0 °C | 3759 psi @Strain 0.400 %, Temperature 104 °F | 50%RH; ISO 11403-1 -2 | |
| 31.12 MPa @Strain 1.10 %, Temperature 150 °C | 4514 psi @Strain 1.10 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 | |
| 34.25 MPa @Strain 0.790 %, Temperature 90.0 °C | 4968 psi @Strain 0.790 %, Temperature 194 °F | DAM; ISO 11403-1 -2 | |
| 37.13 MPa @Strain 0.540 %, Temperature 40.0 °C | 5385 psi @Strain 0.540 %, Temperature 104 °F | DAM; ISO 11403-1 -2 | |
| 41.37 MPa @Strain 0.570 %, Temperature 23.0 °C | 6000 psi @Strain 0.570 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 | |
| 41.5 MPa @Strain 0.470 %, Temperature 23.0 °C | 6020 psi @Strain 0.470 %, Temperature 73.4 °F | DAM; ISO 11403-1 -2 | |
| 42.25 MPa @Strain 1.55 %, Temperature 150 °C | 6128 psi @Strain 1.55 %, Temperature 302 °F | DAM; ISO 11403-1 -2 | |
| 44.11 MPa @Strain 2.01 %, Temperature 150 °C | 6398 psi @Strain 2.01 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 | |
| 44.88 MPa @Strain 1.15 %, Temperature 90.0 °C | 6509 psi @Strain 1.15 %, Temperature 194 °F | 50%RH; ISO 11403-1 -2 | |
| 52.61 MPa @Strain 3.26 %, Temperature 150 °C | 7630 psi @Strain 3.26 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 | |
| 54.28 MPa @Strain 0.980 %, Temperature 40.0 °C | 7873 psi @Strain 0.980 %, Temperature 104 °F | 50%RH; ISO 11403-1 -2 | |
| 55.02 MPa @Strain 2.75 %, Temperature 150 °C | 7980 psi @Strain 2.75 %, Temperature 302 °F | DAM; ISO 11403-1 -2 | |
| 57.51 MPa @Strain 1.63 %, Temperature 90.0 °C | 8341 psi @Strain 1.63 %, Temperature 194 °F | DAM; ISO 11403-1 -2 | |
| 63.12 MPa @Strain 2.08 %, Temperature 90.0 °C | 9155 psi @Strain 2.08 %, Temperature 194 °F | 50%RH; ISO 11403-1 -2 | |
| 63.72 MPa @Strain 0.650 %, Temperature -20.0 °C | 9242 psi @Strain 0.650 %, Temperature -4.00 °F | 50%RH; ISO 11403-1 -2 | |
| 67.98 MPa @Strain 0.820 %, Temperature 0.000 °C | 9860 psi @Strain 0.820 %, Temperature 32.0 °F | 50%RH; ISO 11403-1 -2 | |
| 71.93 MPa @Strain 3.50 %, Temperature 90.0 °C | 10430 psi @Strain 3.50 %, Temperature 194 °F | 50%RH; ISO 11403-1 -2 | |
| 72.3 MPa @Strain 0.770 %, Temperature 0.000 °C | 10500 psi @Strain 0.770 %, Temperature 32.0 °F | DAM; ISO 11403-1 -2 | |
| 73.4 MPa @Strain 1.26 %, Temperature 40.0 °C | 10600 psi @Strain 1.26 %, Temperature 104 °F | DAM; ISO 11403-1 -2 | |
| 73.91 MPa @Strain 1.18 %, Temperature 23.0 °C | 10720 psi @Strain 1.18 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 | |
| 74.49 MPa @Strain 2.80 %, Temperature 90.0 °C | 10800 psi @Strain 2.80 %, Temperature 194 °F | DAM; ISO 11403-1 -2 | |
| 78.89 MPa @Strain 0.830 %, Temperature -20.0 °C | 11440 psi @Strain 0.830 %, Temperature -4.00 °F | DAM; ISO 11403-1 -2 | |
| 79.11 MPa @Strain 1.75 %, Temperature 40.0 °C | 11470 psi @Strain 1.75 %, Temperature 104 °F | 50%RH; ISO 11403-1 -2 | |
| 84.04 MPa @Strain 1.04 %, Temperature 23.0 °C | 12190 psi @Strain 1.04 %, Temperature 73.4 °F | DAM; ISO 11403-1 -2 | |
| 94.42 MPa @Strain 2.82 %, Temperature 40.0 °C | 13690 psi @Strain 2.82 %, Temperature 104 °F | 50%RH; ISO 11403-1 -2 | |
| 100.33 MPa @Strain 1.96 %, Temperature 23.0 °C | 14552 psi @Strain 1.96 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 | |
| 100.68 MPa @Strain 1.34 %, Temperature 0.000 °C | 14602 psi @Strain 1.34 %, Temperature 32.0 °F | 50%RH; ISO 11403-1 -2 | |
| 100.92 MPa @Strain 2.18 %, Temperature 40.0 °C | 14637 psi @Strain 2.18 %, Temperature 104 °F | DAM; ISO 11403-1 -2 | |
| 101.62 MPa @Strain 1.11 %, Temperature -20.0 °C | 14739 psi @Strain 1.11 %, Temperature -4.00 °F | 50%RH; ISO 11403-1 -2 | |
| 118.66 MPa @Strain 1.78 %, Temperature 23.0 °C | 17210 psi @Strain 1.78 %, Temperature 73.4 °F | DAM; ISO 11403-1 -2 | |
| 120.54 MPa @Strain 1.46 %, Temperature 0.000 °C | 17483 psi @Strain 1.46 %, Temperature 32.0 °F | DAM; ISO 11403-1 -2 | |
| 127.28 MPa @Strain 1.98 %, Temperature 0.000 °C | 18460 psi @Strain 1.98 %, Temperature 32.0 °F | 50%RH; ISO 11403-1 -2 | |
| 134.63 MPa @Strain 1.66 %, Temperature -20.0 °C | 19526 psi @Strain 1.66 %, Temperature -4.00 °F | 50%RH; ISO 11403-1 -2 | |
| 142.85 MPa @Strain 1.74 %, Temperature -20.0 °C | 20719 psi @Strain 1.74 %, Temperature -4.00 °F | DAM; ISO 11403-1 -2 | |
| 157.09 MPa @Strain 2.33 %, Temperature 0.000 °C | 22784 psi @Strain 2.33 %, Temperature 32.0 °F | DAM; ISO 11403-1 -2 | |
| 伸长率 (断裂) | 2.0 % | 2.0 % | DAM; ISO 527-1/-2 |
| 2.6 % | 2.6 % | 50%RH; ISO 527-1/-2 | |
| 拉伸模量 | 7.50 GPa | 1090 ksi | 50%RH; ISO 527-1/-2 |
| 9.00 GPa | 1310 ksi | DAM; ISO 527-1/-2 | |
| 3.213 GPa @Temperature 150 °C | 466.0 ksi @Temperature 302 °F | 50%RH; ISO 11403-1 -2 | |
| 3.595 GPa @Temperature 150 °C | 521.4 ksi @Temperature 302 °F | DAM; ISO 11403-1 -2 | |
| 5.515 GPa @Temperature 60.0 °C | 799.9 ksi @Temperature 140 °F | 50%RH; ISO 11403-1 -2 | |
| 5.62 GPa @Temperature 60.0 °C | 815 ksi @Temperature 140 °F | DAM; ISO 11403-1 -2 | |
| 10.386 GPa @Temperature -20.0 °C | 1506.4 ksi @Temperature -4.00 °F | 50%RH; ISO 11403-1 -2 | |
| 10.498 GPa @Temperature -20.0 °C | 1522.6 ksi @Temperature -4.00 °F | DAM; ISO 11403-1 -2 | |
| 割线模量 | 4.16 GPa @Strain 2.06 %, Temperature 40.0 °C | 603 ksi @Strain 2.06 %, Temperature 104 °F | 50%RH; ISO 11403-1 -2 |