| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|
| 抗张强度(断裂) | 63.0 MPa | 9140 psi | 50%RH; ISO 527-1/-2 |
| 90.0 MPa | 13100 psi | DAM; ISO 527-1/-2 |
| 抗张强度 | 3.93 MPa @Strain 0.500 %, Temperature 150 °C | 570 psi @Strain 0.500 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 |
| 6.20 MPa @Strain 0.700 %, Temperature 150 °C | 899 psi @Strain 0.700 %, Temperature 302 °F | DAM; ISO 11403-1 -2 |
| 10.38 MPa @Strain 1.70 %, Temperature 150 °C | 1505 psi @Strain 1.70 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 |
| 11.76 MPa @Strain 0.500 %, Temperature 23.0 °C | 1706 psi @Strain 0.500 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 |
| 16.06 MPa @Strain 3.50 %, Temperature 150 °C | 2329 psi @Strain 3.50 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 |
| 17.0 MPa @Strain 2.70 %, Temperature 150 °C | 2470 psi @Strain 2.70 %, Temperature 302 °F | DAM; ISO 11403-1 -2 |
| 19.0 MPa @Strain 5.00 %, Temperature 150 °C | 2760 psi @Strain 5.00 %, Temperature 302 °F | 50%RH; ISO 11403-1 -2 |
| 19.43 MPa @Strain 0.300 %, Temperature -40.0 °C | 2818 psi @Strain 0.300 %, Temperature -40.0 °F | DAM; ISO 11403-1 -2 |
| 20.27 MPa @Strain 1.00 %, Temperature 23.0 °C | 2940 psi @Strain 1.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 |
| 24.6 MPa @Strain 6.00 %, Temperature 150 °C | 3570 psi @Strain 6.00 %, Temperature 302 °F | DAM; ISO 11403-1 -2 |
| 27.27 MPa @Strain 0.500 %, Temperature 0.000 °C | 3955 psi @Strain 0.500 %, Temperature 32.0 °F | 50%RH; ISO 11403-1 -2 |
| 29.7 MPa @Strain 13.0 %, Temperature 150 °C | 4310 psi @Strain 13.0 %, Temperature 302 °F | DAM; ISO 11403-1 -2 |
| 30.03 MPa @Strain 1.90 %, Temperature 23.0 °C | 4355 psi @Strain 1.90 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 |
| 30.3 MPa @Strain 0.500 %, Temperature 0.000 °C | 4390 psi @Strain 0.500 %, Temperature 32.0 °F | DAM; ISO 11403-1 -2 |
| 33.3 MPa @Strain 0.600 %, Temperature 23.0 °C | 4830 psi @Strain 0.600 %, Temperature 73.4 °F | DAM; ISO 11403-1 -2 |
| 36.3 MPa @Strain 0.500 %, Temperature -40.0 °C | 5260 psi @Strain 0.500 %, Temperature -40.0 °F | 50%RH; ISO 11403-1 -2 |
| 42.11 MPa @Strain 3.90 %, Temperature 23.0 °C | 6108 psi @Strain 3.90 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 |
| 56.33 MPa @Strain 0.900 %, Temperature -40.0 °C | 8170 psi @Strain 0.900 %, Temperature -40.0 °F | DAM; ISO 11403-1 -2 |
| 58.6 MPa @Strain 1.10 %, Temperature 23.0 °C | 8500 psi @Strain 1.10 %, Temperature 73.4 °F | DAM; ISO 11403-1 -2 |
| 61.78 MPa @Strain 1.20 %, Temperature 0.000 °C | 8960 psi @Strain 1.20 %, Temperature 32.0 °F | 50%RH; ISO 11403-1 -2 |
| 63.9 MPa @Strain 1.10 %, Temperature 0.000 °C | 9270 psi @Strain 1.10 %, Temperature 32.0 °F | DAM; ISO 11403-1 -2 |
| 64.161 MPa @Strain 35.0 %, Temperature 23.0 °C | 9305.8 psi @Strain 35.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 |
| 66.1 MPa @Strain 1.00 %, Temperature -40.0 °C | 9590 psi @Strain 1.00 %, Temperature -40.0 °F | 50%RH; ISO 11403-1 -2 |
| 70.7 MPa @Strain 1.40 %, Temperature 23.0 °C | 10300 psi @Strain 1.40 %, Temperature 73.4 °F | DAM; ISO 11403-1 -2 |
| 76.3 MPa @Strain 1.60 %, Temperature 0.000 °C | 11100 psi @Strain 1.60 %, Temperature 32.0 °F | 50%RH; ISO 11403-1 -2 |
| 78.05 MPa @Strain 1.30 %, Temperature -40.0 °C | 11320 psi @Strain 1.30 %, Temperature -40.0 °F | DAM; ISO 11403-1 -2 |
| 79.8 MPa @Strain 1.30 %, Temperature -40.0 °C | 11600 psi @Strain 1.30 %, Temperature -40.0 °F | 50%RH; ISO 11403-1 -2 |
| 80.8 MPa @Strain 1.80 %, Temperature 23.0 °C | 11700 psi @Strain 1.80 %, Temperature 73.4 °F | DAM; ISO 11403-1 -2 |
| 81.1 MPa @Strain 1.50 %, Temperature 0.000 °C | 11800 psi @Strain 1.50 %, Temperature 32.0 °F | DAM; ISO 11403-1 -2 |
| 84.38 MPa @Strain 1.90 %, Temperature 0.000 °C | 12240 psi @Strain 1.90 %, Temperature 32.0 °F | 50%RH; ISO 11403-1 -2 |
| 90.91 MPa @Strain 3.70 %, Temperature 23.0 °C | 13190 psi @Strain 3.70 %, Temperature 73.4 °F | DAM; ISO 11403-1 -2 |
| 93.5 MPa @Strain 1.70 %, Temperature -40.0 °C | 13600 psi @Strain 1.70 %, Temperature -40.0 °F | 50%RH; ISO 11403-1 -2 |
| 93.7 MPa @Strain 1.90 %, Temperature 0.000 °C | 13600 psi @Strain 1.90 %, Temperature 32.0 °F | DAM; ISO 11403-1 -2 |
| 96.12 MPa @Strain 1.70 %, Temperature -40.0 °C | 13940 psi @Strain 1.70 %, Temperature -40.0 °F | DAM; ISO 11403-1 -2 |
| 99.88 MPa @Strain 4.40 %, Temperature 0.000 °C | 14490 psi @Strain 4.40 %, Temperature 32.0 °F | 50%RH; ISO 11403-1 -2 |
| 112.7 MPa @Strain 4.30 %, Temperature 0.000 °C | 16350 psi @Strain 4.30 %, Temperature 32.0 °F | DAM; ISO 11403-1 -2 |
| 119.4 MPa @Strain 4.90 %, Temperature -40.0 °C | 17320 psi @Strain 4.90 %, Temperature -40.0 °F | 50%RH; ISO 11403-1 -2 |
| 128.4 MPa @Strain 3.10 %, Temperature -40.0 °C | 18620 psi @Strain 3.10 %, Temperature -40.0 °F | DAM; ISO 11403-1 -2 |
| 伸长率 (断裂) | 10 % | 10 % | DAM; ISO 527-1/-2 |
| 35 % | 35 % | 50%RH; ISO 527-1/-2 |
| 拉伸模量 | 2.60 GPa | 377 ksi | 50%RH; ISO 527-1/-2 |
| 5.90 GPa | 856 ksi | DAM; ISO 527-1/-2 |
| 弯曲模量 | 2.00 GPa | 290 ksi | 50%RH; ISO 178 |
| 5.40 GPa | 783 ksi | DAM; ISO 178 |
| 割线模量 | 0.25895 GPa @Strain 20.0 %, Temperature 80.0 °C | 37.558 ksi @Strain 20.0 %, Temperature 176 °F | DAM; ISO 11403-1 -2 |
| 0.261 GPa @Strain 14.0 %, Temperature 100 °C | 37.9 ksi @Strain 14.0 %, Temperature 212 °F | 50%RH; ISO 11403-1 -2 |
| 0.331 GPa @Strain 12.0 %, Temperature 80.0 °C | 48.0 ksi @Strain 12.0 %, Temperature 176 °F | 50%RH; ISO 11403-1 -2 |
| 0.3315 GPa @Strain 12.0 %, Temperature 100 °C | 48.08 ksi @Strain 12.0 %, Temperature 212 °F | DAM; ISO 11403-1 -2 |
| 0.454 GPa @Strain 13.0 %, Temperature 23.0 °C | 65.8 ksi @Strain 13.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 |
| 0.510 GPa @Strain 6.50 %, Temperature 100 °C | 73.9 ksi @Strain 6.50 %, Temperature 212 °F | DAM; ISO 11403-1 -2 |
| 0.516 GPa @Strain 8.00 %, Temperature 80.0 °C | 74.9 ksi @Strain 8.00 %, Temperature 176 °F | DAM; ISO 11403-1 -2 |
| 0.533 GPa @Strain 5.50 %, Temperature 100 °C | 77.3 ksi @Strain 5.50 %, Temperature 212 °F | 50%RH; ISO 11403-1 -2 |
| 0.548 GPa @Strain 6.00 %, Temperature 80.0 °C | 79.5 ksi @Strain 6.00 %, Temperature 176 °F | 50%RH; ISO 11403-1 -2 |
| 0.601 GPa @Strain 4.60 %, Temperature 100 °C | 87.1 ksi @Strain 4.60 %, Temperature 212 °F | DAM; ISO 11403-1 -2 |
| 0.707 GPa @Strain 3.10 %, Temperature 100 °C | 103 ksi @Strain 3.10 %, Temperature 212 °F | 50%RH; ISO 11403-1 -2 |
| 0.758 GPa @Strain 3.30 %, Temperature 80.0 °C | 110 ksi @Strain 3.30 %, Temperature 176 °F | 50%RH; ISO 11403-1 -2 |
| 0.792 GPa @Strain 3.70 %, Temperature 80.0 °C | 115 ksi @Strain 3.70 %, Temperature 176 °F | DAM; ISO 11403-1 -2 |
| 0.800 GPa @Strain 2.20 %, Temperature 100 °C | 116 ksi @Strain 2.20 %, Temperature 212 °F | DAM; ISO 11403-1 -2 |