- 技术参数
-
|
性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
|
物理性能 |
比重 |
|
ASTM D-792 |
1.64 |
|
|
模具收缩率 |
3.2mm(0.126in) |
ASTM D-955 |
0.5 |
% |
|
机械性能 |
弯曲强度 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-790 |
125 |
MPa |
|
断裂伸长率 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-638 |
4 |
% |
|
弯曲模量 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-790 |
9600 |
MPa |
|
弯曲模量 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-790 |
9600 |
MPa |
|
弯曲模量 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-790 |
13900 |
MPa |
|
拉伸模量 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-638 |
11569 |
MPa |
|
拉伸强度 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-638 |
141 |
MPa |
|
断裂伸长率 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-638 |
3.3 |
% |
|
压缩模量 |
|
ASTM D-695 |
4100 |
MPa |
|
弯曲强度 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-790 |
125 |
MPa |
|
IZOD冲击强度 |
3.2mm(0.126in) |
ASTM D-256 |
160 |
J/m |
|
断裂伸长率 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-638 |
4 |
% |
|
拉伸模量 |
3.2mm |
ASTM D-638 |
10500 |
MPa |
|
拉伸模量 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-638 |
11569 |
MPa |
|
压缩模量 |
|
ASTM D-695 |
4100 |
MPa |
|
弯曲强度 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-790 |
158 |
MPa |
|
弯曲模量 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-790 |
13900 |
MPa |
|
拉伸模量 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-638 |
10500 |
MPa |
|
IZOD冲击强度 |
3.2mm(0.126in) |
ASTM D-256 |
160 |
J/m |
|
弯曲强度 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-790 |
158 |
MPa |
|
拉伸强度 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-638 |
125 |
MPa |
|
电气性能 |
损耗因数 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-2520 B |
0.001 |
|
|
损耗因数 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-2520 B |
0.002 |
|
|
介电强度 |
0.8mm |
ASTM D-149 |
49 |
Kv/mm |
|
介电常数 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-2520 B |
3.9 |
|
|
介电常数 |
0.8mm(0.032in) |
ASTM D-150 |
2.9 |
|
|
介电常数 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-2520 B |
4 |
|
|
损耗因数 |
0.8mm(0.032in) |
ASTM D-150 |
0.013 |
|
|
介电强度 |
3.2mm |
ASTM D-149 |
26 |
Kv/mm |
|
介电常数 |
0.8mm |
ASTM D-150 |
3.3 |
|
|
介电常数 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-2520 B |
4.1 |
|
|
介电常数 |
3.2mm(0.125in) |
ASTM D-150 |
3.6 |
|
|
介电强度 |
1.6mm |
ASTM D-149 |
41 |
Kv/mm |
|
损耗因数 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-2520 B |
0.001 |
|
|
介电常数 |
3.2mm(0.125in) |
ASTM D-150 |
3.6 |
|
|
损耗因数 |
0.8mm(0.032in) |
ASTM D-150 |
0.029 |
|
|
损耗因数 |
0.8mm(0.032in) |
ASTM D-150 |
0.009 |
|
|
损耗因数 |
3.2mm(0.125in) |
ASTM D-150 |
0.013 |
|
|
介电常数 |
0.8mm(0.032in) |
ASTM D-150 |
3.3 |
|
|
表面电阻率 |
|
ASTM D-257 |
>1×1016 |
Ohm |
|
介电常数 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-2520 B |
3.9 |
|
|
介电常数 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-2520 B |
4.1 |
|
|
体积电阻率 |
|
ASTM D-257 |
>1×1016 |
Ohm-cm |
|
损耗因数 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-2520 B |
0.002 |
|
|
损耗因数 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-2520 B |
0.002 |
|
|
损耗因数 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-2520 B |
0.001 |
|
|
介电常数 |
3.2mm(0.125in) |
ASTM D-150 |
3.2 |
|
|
介电常数 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-2520 B |
3.9 |
|
|
损耗因数 |
3.2mm(0.125in) |
ASTM D-150 |
0.028 |
|
|
加工性能 |
损耗因数 |
3.2mm(0.125in) |
ASTM D-150 |
0.008 |
|
|
热性能 |
热变形温度 |
1.80MPa |
ASTM D-648 |
239 |
℃ |
|
玻璃化转变温度 |
|
ASTM D-3418 |
120 |
℃ |
|
模压温度范围 |
|
|
30-95 |
℃ |
|
干燥温度 |
|
|
135 |
℃ |
|
熔点 |
|
ASTM D-3418 |
335 |
℃ |
|
解链温度范围 |
|
|
350-360 |
℃ |
|
其它性能 |
工业含水量 |
|
|
<0.01 |
% |
|
RTI,Electrical |
1.5mm |
UL 746-B |
130 |
℃ |
|
RTI,Mechanical with Impact |
1.5mm |
UL 746-B |
130 |
℃ |
|
RTI,Mechanical without Impact |
1.5mm |
UL 746-B |
130 |
℃ |