牌号分类
GRADE PHYSICAL PROPERTY
品种：TPU丨IROGRAN® A 60 E 4902
- 规格用途
-
- 技术参数
-
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重2 |
|
ASTMD792 |
1.14 |
g/cm³ |
| 物理性能 |
密度3 |
|
DIN53478 |
1.14 |
g/cm³ |
| 物理性能 |
MeltVolume-FlowRate(MVR)(160°C/8.7kg) |
|
|
35.0 |
cm³/10min |
| 机械性能 |
Abrasion2 |
-- |
DIN53516 |
43 |
mm³ |
| 机械性能 |
Abrasion2 |
-- |
ASTMD395 |
43 |
mm³ |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
TensileSet3(200%Strain) |
|
ASTMD412 |
8 |
% |
| ELASTOMERS |
TensileSet3(200%Strain) |
|
DIN53504 |
8 |
% |
| ELASTOMERS |
TensileStress4(100%Strain,0.635mm) |
|
ASTMD412 |
2.34 |
MPa |
| ELASTOMERS |
TensileStress4(100%Strain,0.635mm) |
|
DIN53504 |
1.40 |
MPa |
| ELASTOMERS |
TensileStress4(300%Strain,0.635mm) |
|
ASTMD412 |
4.07 |
MPa |
| ELASTOMERS |
TensileStress4(300%Strain,0.635mm) |
|
DIN53504 |
2.40 |
MPa |
| ELASTOMERS |
TensileStrength4(Break,0.635mm) |
|
ASTMD412 |
7.52 |
MPa |
| ELASTOMERS |
TensileStress4(Break,0.635mm) |
|
DIN53504 |
10.0 |
MPa |
| ELASTOMERS |
TensileElongation4(Break,0.635mm) |
|
ASTMD412 |
720 |
% |
| ELASTOMERS |
TensileElongation4(Break,0.635mm) |
|
DIN53504 |
900 |
% |
| ELASTOMERS |
TearStrength4(0.635mm) |
|
ASTMD624 |
35.9 |
kN/m |
| ELASTOMERS |
TearStrength4(0.635mm) |
|
DIN53515 |
25 |
kN/m |
| ELASTOMERS |
压缩永久变形2 |
23°C,70hr |
ASTMD395 |
40 |
% |
| ELASTOMERS |
压缩永久变形2 |
70°C,24hr |
ASTMD395 |
80 |
% |
| ELASTOMERS |
压缩永久变形2 |
23°C,70hr |
DIN53517 |
35 |
% |
| ELASTOMERS |
压缩永久变形2 |
70°C,24hr |
DIN53517 |
60 |
% |
| ELASTOMERS |
巴肖氏弹性 |
|
ASTMD2632 |
60 |
% |
| 硬度 |
肖氏硬度 |
邵氏A,注塑 |
ASTMD2240 |
56 |
|
| 硬度 |
肖氏硬度 |
邵氏D,注塑 |
ASTMD2240 |
15 |
|
| 硬度 |
肖氏硬度 |
邵氏A,注塑 |
DIN53505 |
55 |
|
| 硬度 |
肖氏硬度 |
邵氏D,注塑 |
DIN53505 |
15 |
|
| 热性能 |
熔融温度 |
|
InternalMethod |
98.9to130 |
°C |
| 热性能 |
TMA4 |
High:635.0µm |
InternalMethod |
145 |
°C |
| 热性能 |
TMA4 |
Low:635.0µm |
InternalMethod |
110 |
°C |