规格级别 | 外观颜色 | ||
该料用途 | |||
备注说明 |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 | 密度 | ASTMD1505 | 0.937 | g/cm³ | |
物理性能 | 熔流率(熔体流动速率) | 190°C/2.16kg | ASTMD1238 | 0.30 | g/10min |
物理性能 | 熔流率(熔体流动速率) | 190°C/21.6kg | ASTMD1238 | 20 | g/10min |
薄膜 | 薄膜厚度-经测试 | 13 | µm | ||
薄膜 | 可供应的薄膜厚度 | Minimum12µm(0.5mil) | |||
薄膜 | SecantModulus-1%Secant,MD2(13µm) | ASTMD882 | 790 | MPa | |
薄膜 | SecantModulus-1%Secant,TD2(13µm) | ASTMD882 | 965 | MPa | |
薄膜 | TensileStrength-MD2(Yield,13µm) | ASTMD882 | 21.0 | MPa | |
薄膜 | TensileStrength-TD2(Yield,13µm) | ASTMD882 | 21.0 | MPa | |
薄膜 | TensileStrength-MD2(Break,13µm) | ASTMD882 | 42.0 | MPa | |
薄膜 | TensileStrength-TD2(Break,13µm) | ASTMD882 | 41.0 | MPa | |
薄膜 | TensileElongation-MD2(Break,13µm) | ASTMD882 | 500 | % | |
薄膜 | TensileElongation-TD2(Break,13µm) | ASTMD882 | 600 | % | |
薄膜 | DartDropImpact3(13µm) | ASTMD1709A | 110 | g | |
薄膜 | ElmendorfTearStrength-MD(13µm) | ASTMD1922 | 50 | g | |
薄膜 | ElmendorfTearStrength-TD(13µm) | ASTMD1922 | 500 | g | |
热性能 | 熔融峰值温度 | ASTMD3417 | 125 | °C |