牌号分类
GRADE PHYSICAL PROPERTY
- 规格用途
-
- 技术参数
-
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.918 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
2.0 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
ASTMD746 |
30 |
µm |
| 薄膜 |
抗张强度 |
MD:屈服,30µm |
ASTMD882 |
9.81 |
MPa |
| 薄膜 |
抗张强度 |
TD:屈服,30µm |
ASTMD882 |
9.81 |
MPa |
| 薄膜 |
抗张强度 |
MD:断裂,30µm |
ASTMD882 |
46.1 |
MPa |
| 薄膜 |
抗张强度 |
TD:断裂,30µm |
ASTMD882 |
42.2 |
MPa |
| 薄膜 |
伸长率 |
MD:断裂,30µm |
ASTMD882 |
700 |
% |
| 薄膜 |
伸长率 |
TD:断裂,30µm |
ASTMD882 |
750 |
% |
| 薄膜 |
SpencerImpact(30.0µm) |
|
ASTMD3420 |
0.785 |
J |
| 薄膜 |
薄膜厚度-经测试 |
|
ASTMD746 |
30 |
µm |
| 薄膜 |
抗张强度 |
MD:屈服,30µm |
ASTMD882 |
9.81 |
MPa |
| 薄膜 |
抗张强度 |
TD:屈服,30µm |
ASTMD882 |
9.81 |
MPa |
| 薄膜 |
抗张强度 |
MD:断裂,30µm |
ASTMD882 |
46.1 |
MPa |
| 薄膜 |
抗张强度 |
TD:断裂,30µm |
ASTMD882 |
42.2 |
MPa |
| 薄膜 |
伸长率 |
MD:断裂,30µm |
ASTMD882 |
700 |
% |
| 薄膜 |
伸长率 |
TD:断裂,30µm |
ASTMD882 |
750 |
% |
| 薄膜 |
SpencerImpact(30.0µm) |
|
ASTMD3420 |
0.785 |
J |
| 热性能 |
脆化温度 |
|
ASTMD746 |
<-80.0 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
100 |
°C |
| 光学性能 |
雾度(30.0µm) |
|
ASTMD1003 |
2.0 |
% |
| 补充信息 |
撕裂强度 |
MD:30.0µm |
ASTMD1922 |
186.3 |
kN/m |
| 补充信息 |
撕裂强度 |
TD:30.0µm |
ASTMD1922 |
196.1 |
kN/m |