| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.09 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）2(265°C/5.0kg) |
|
ASTMD1238 |
37 |
g/10min |
| 物理性能 |
MoldingShrinkage-Flow(23°C,3.18mm,InjectionMolded) |
|
ASTMD955 |
0.50to0.70 |
% |
| 机械性能 |
抗张强度3 |
Yield,23°C,3.18mm,InjectionMolded4 |
ASTMD638 |
42.2 |
MPa |
| 机械性能 |
抗张强度3 |
Yield,23°C,3.18mm,InjectionMolded5 |
ASTMD638 |
43.6 |
MPa |
| 机械性能 |
抗张强度 |
Break,23°C,3.18mm,InjectionMolded7 |
ASTMD638 |
35.9 |
MPa |
| 机械性能 |
抗张强度 |
Break,23°C,3.18mm,InjectionMolded8 |
ASTMD638 |
39.4 |
MPa |
| 机械性能 |
伸长率6 |
Yield,23°C,3.18mm,InjectionMolded7 |
ASTMD638 |
3.7 |
% |
| 机械性能 |
伸长率6 |
Yield,23°C,3.18mm,InjectionMolded8 |
ASTMD638 |
3.6 |
% |
| 机械性能 |
伸长率6 |
Break,23°C,3.18mm,InjectionMolded7 |
ASTMD638 |
15 |
% |
| 机械性能 |
伸长率6 |
Break,23°C,3.18mm,InjectionMolded8 |
ASTMD638 |
200 |
% |
| 机械性能 |
FlexuralModulus-Tangent9(23°C,3.18mm,InjectionMolded,50.8mmSpan) |
|
ASTMD790B |
1480 |
MPa |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C,3.18mm,注塑) |
|
ASTMD256A |
NoBreak |
|
| 热性能 |
DeflectionTemperatureUnderLoad(1.8MPa,Unannealed,3.18mm,InjectionMolded) |
|
ASTMD648 |
52.8 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD152510 |
143 |
°C |