牌号分类
GRADE PHYSICAL PROPERTY
- 规格用途
-
- 技术参数
-
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.925 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
1.0 |
g/10min |
| 机械性能 |
摩擦系数(吹塑薄膜) |
|
ASTMD1894 |
0.150.13 |
|
| 薄膜 |
薄膜厚度-经测试 |
|
|
2850 |
µm |
| 薄膜 |
割线模量 |
2%正割,MD:28µm |
ASTMD882 |
210 |
MPa |
| 薄膜 |
割线模量 |
2%正割,MD:50µm |
ASTMD882 |
220 |
MPa |
| 薄膜 |
割线模量 |
2%正割,TD:28µm |
ASTMD882 |
220 |
MPa |
| 薄膜 |
割线模量 |
2%正割,TD:50µm |
ASTMD882 |
240 |
MPa |
| 薄膜 |
抗张强度 |
MD:屈服,28µm |
ASTMD882 |
9.00 |
MPa |
| 薄膜 |
抗张强度 |
MD:屈服,50µm |
ASTMD882 |
10.0 |
MPa |
| 薄膜 |
抗张强度 |
TD:屈服,28µm |
ASTMD882 |
12.0 |
MPa |
| 薄膜 |
抗张强度 |
TD:屈服,50µm |
ASTMD882 |
12.0 |
MPa |
| 薄膜 |
抗张强度 |
MD:断裂,28µm |
ASTMD882 |
28.0 |
MPa |
| 薄膜 |
抗张强度 |
MD:断裂,50µm |
ASTMD882 |
34.0 |
MPa |
| 薄膜 |
抗张强度 |
TD:断裂,28µm |
ASTMD882 |
24.0 |
MPa |
| 薄膜 |
抗张强度 |
TD:断裂,50µm |
ASTMD882 |
30.0 |
MPa |
| 薄膜 |
伸长率 |
MD:断裂,28µm |
ASTMD882 |
750 |
% |
| 薄膜 |
伸长率 |
MD:断裂,50µm |
ASTMD882 |
1000 |
% |
| 薄膜 |
伸长率 |
TD:断裂,28µm |
ASTMD882 |
800 |
% |
| 薄膜 |
伸长率 |
TD:断裂,50µm |
ASTMD882 |
1000 |
% |
| 薄膜 |
落锤冲击 |
28µm,吹塑薄膜 |
ASTMD1709 |
130 |
g |
| 薄膜 |
落锤冲击 |
50µm,吹塑薄膜 |
ASTMD1709 |
240 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
MD:28µm |
ASTMD1922 |
310 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
MD:50µm |
ASTMD1922 |
590 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
TD:28µm |
ASTMD1922 |
510 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
TD:50µm |
ASTMD1922 |
980 |
g |
| 薄膜 |
薄膜厚度-经测试 |
|
|
2850 |
µm |
| 薄膜 |
割线模量 |
2%正割,MD:28µm |
ASTMD882 |
210 |
MPa |
| 薄膜 |
割线模量 |
2%正割,MD:50µm |
ASTMD882 |
220 |
MPa |
| 薄膜 |
割线模量 |
2%正割,TD:28µm |
ASTMD882 |
220 |
MPa |
| 薄膜 |
割线模量 |
2%正割,TD:50µm |
ASTMD882 |
240 |
MPa |
| 薄膜 |
抗张强度 |
MD:屈服,28µm |
ASTMD882 |
9.00 |
MPa |
| 薄膜 |
抗张强度 |
MD:屈服,50µm |
ASTMD882 |
10.0 |
MPa |
| 薄膜 |
抗张强度 |
TD:屈服,28µm |
ASTMD882 |
12.0 |
MPa |
| 薄膜 |
抗张强度 |
TD:屈服,50µm |
ASTMD882 |
12.0 |
MPa |
| 薄膜 |
抗张强度 |
MD:断裂,28µm |
ASTMD882 |
28.0 |
MPa |
| 薄膜 |
抗张强度 |
MD:断裂,50µm |
ASTMD882 |
34.0 |
MPa |
| 薄膜 |
抗张强度 |
TD:断裂,28µm |
ASTMD882 |
24.0 |
MPa |
| 薄膜 |
抗张强度 |
TD:断裂,50µm |
ASTMD882 |
30.0 |
MPa |
| 薄膜 |
伸长率 |
MD:断裂,28µm |
ASTMD882 |
750 |
% |
| 薄膜 |
伸长率 |
MD:断裂,50µm |
ASTMD882 |
1000 |
% |
| 薄膜 |
伸长率 |
TD:断裂,28µm |
ASTMD882 |
800 |
% |
| 薄膜 |
伸长率 |
TD:断裂,50µm |
ASTMD882 |
1000 |
% |
| 薄膜 |
落锤冲击 |
28µm,吹塑薄膜 |
ASTMD1709 |
130 |
g |
| 薄膜 |
落锤冲击 |
50µm,吹塑薄膜 |
ASTMD1709 |
240 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
MD:28µm |
ASTMD1922 |
310 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
MD:50µm |
ASTMD1922 |
590 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
TD:28µm |
ASTMD1922 |
510 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
TD:50µm |
ASTMD1922 |
980 |
g |
| 光学性能 |
光泽度 |
28.0µm,吹塑薄膜 |
ASTMD2457 |
72 |
|
| 光学性能 |
光泽度 |
50.0µm,吹塑薄膜 |
ASTMD2457 |
74 |
|
| 光学性能 |
雾度 |
28.0µm,吹塑薄膜 |
ASTMD1003 |
8.0 |
% |
| 光学性能 |
雾度 |
50.0µm,吹塑薄膜 |
ASTMD1003 |
10 |
% |