品种：LDPE丨VENELENE® FB-3003
- 规格用途
-
- 技术参数
-
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.922 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.27 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
35 |
µm |
| 薄膜 |
膜刺穿力(35µm) |
|
ASTMD3420 |
14.1 |
N |
| 薄膜 |
抗张强度 |
MD:断裂,35µm |
ASTMD882 |
20.0 |
MPa |
| 薄膜 |
抗张强度 |
TD:断裂,35µm |
ASTMD882 |
19.0 |
MPa |
| 薄膜 |
伸长率 |
MD:断裂,100µm |
ASTMD882 |
35 |
% |
| 薄膜 |
伸长率 |
TD:断裂,35µm |
ASTMD882 |
500 |
% |
| 薄膜 |
埃尔曼多夫抗撕强度 |
MD:35µm |
ASTMD1922 |
200 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
TD:35µm |
ASTMD1922 |
250 |
g |
| 薄膜 |
ImpactResistance,Film |
|
ASTMD1709 |
280 |
J/cm |
| 薄膜 |
Toughness,Film |
MD |
ASTMD882 |
48.0 |
MPa |
| 薄膜 |
Toughness,Film |
TD |
ASTMD882 |
62.0 |
MPa |
| 薄膜 |
薄膜厚度-经测试 |
|
|
35 |
µm |
| 薄膜 |
膜刺穿力(35µm) |
|
ASTMD3420 |
14.1 |
N |
| 薄膜 |
抗张强度 |
MD:断裂,35µm |
ASTMD882 |
20.0 |
MPa |
| 薄膜 |
抗张强度 |
TD:断裂,35µm |
ASTMD882 |
19.0 |
MPa |
| 薄膜 |
伸长率 |
MD:断裂,100µm |
ASTMD882 |
35 |
% |
| 薄膜 |
伸长率 |
TD:断裂,35µm |
ASTMD882 |
500 |
% |
| 薄膜 |
埃尔曼多夫抗撕强度 |
MD:35µm |
ASTMD1922 |
200 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
TD:35µm |
ASTMD1922 |
250 |
g |
| 薄膜 |
ImpactResistance,Film |
|
ASTMD1709 |
280 |
J/cm |
| 薄膜 |
Toughness,Film |
MD |
ASTMD882 |
48.0 |
MPa |
| 薄膜 |
Toughness,Film |
TD |
ASTMD882 |
62.0 |
MPa |
| 光学性能 |
透射率(35.0µm) |
|
ASTMD1003 |
66.0 |
% |
| 光学性能 |
雾度(35.0µm) |
|
ASTMD1003 |
31 |
% |