品种:LDPE丨VENELENE® FB-7000
- 规格用途
-
- 技术参数
-
性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
物理性能 |
比重 |
|
ASTMD792 |
0.922 |
g/cm³ |
物理性能 |
熔流率(熔体流动速率)(190°C/2.16kg) |
|
ASTMD1238 |
0.80 |
g/10min |
薄膜 |
薄膜厚度-经测试 |
|
|
100 |
µm |
薄膜 |
膜刺穿力(100µm) |
|
ASTMD3420 |
10.8 |
N |
薄膜 |
抗张强度 |
MD:断裂,100µm |
ASTMD882 |
23.0 |
MPa |
薄膜 |
抗张强度 |
TD:断裂,100µm |
ASTMD882 |
18.0 |
MPa |
薄膜 |
伸长率 |
MD:断裂,100µm |
ASTMD882 |
200 |
% |
薄膜 |
伸长率 |
TD:断裂,100µm |
ASTMD882 |
520 |
% |
薄膜 |
埃尔曼多夫抗撕强度 |
MD:100µm |
ASTMD1922 |
400 |
g |
薄膜 |
埃尔曼多夫抗撕强度 |
TD:100µm |
ASTMD1922 |
150 |
g |
薄膜 |
ImpactResistance,Film |
|
ASTMD1709 |
290 |
J/cm |
薄膜 |
Toughness,Film |
MD |
ASTMD882 |
40.0 |
MPa |
薄膜 |
Toughness,Film |
TD |
ASTMD882 |
60.0 |
MPa |
薄膜 |
薄膜厚度-经测试 |
|
|
100 |
µm |
薄膜 |
膜刺穿力(100µm) |
|
ASTMD3420 |
10.8 |
N |
薄膜 |
抗张强度 |
MD:断裂,100µm |
ASTMD882 |
23.0 |
MPa |
薄膜 |
抗张强度 |
TD:断裂,100µm |
ASTMD882 |
18.0 |
MPa |
薄膜 |
伸长率 |
MD:断裂,100µm |
ASTMD882 |
200 |
% |
薄膜 |
伸长率 |
TD:断裂,100µm |
ASTMD882 |
520 |
% |
薄膜 |
埃尔曼多夫抗撕强度 |
MD:100µm |
ASTMD1922 |
400 |
g |
薄膜 |
埃尔曼多夫抗撕强度 |
TD:100µm |
ASTMD1922 |
150 |
g |
薄膜 |
ImpactResistance,Film |
|
ASTMD1709 |
290 |
J/cm |
薄膜 |
Toughness,Film |
MD |
ASTMD882 |
40.0 |
MPa |
薄膜 |
Toughness,Film |
TD |
ASTMD882 |
60.0 |
MPa |
光学性能 |
透射率(100µm) |
|
ASTMD1003 |
78.0 |
% |
光学性能 |
雾度(100µm) |
|
ASTMD1003 |
17 |
% |